TPGT 16T308 EN P25

cutting data

Indexable Insert

Order Code:

(Corresponding ANSI size: TPGT 32.52)

View in Online Store

Tungsten Carbide – Substrate
EN – Geometry
P25 – Grade

Turning

0.06 mm - 4 mm – ap
0.0024" - 0.1575" – DOC

Milling

0.06 mm - 15 mm – ap
0.0024" - 0.5906" – DOC

Turning - metric starting values

Material	v_{c max}	v_{c min}	f_max	f_min
P1 Low Carbon Steel	150 m/min	90 m/min	0.4 mm	0.06 mm
P2 Alloy Steel	120 m/min	60 m/min	0.25 mm	0.06 mm
P3 Tool Steel	90 m/min	50 m/min	0.25 mm	0.06 mm
P4 Alloy Tool Steel	0 m/min	0 m/min	0 mm	0 mm
P5 Alloy Cast Steel	0 m/min	0 m/min	0 mm	0 mm
M1 Stainless Steel	0 m/min	0 m/min	0 mm	0 mm
M2 Stainless Steel - Austenitic, Martensitic	0 m/min	0 m/min	0 mm	0 mm
K1 Grey Cast Iron	0 m/min	0 m/min	0 mm	0 mm
K2 Cast Iron Malleable	0 m/min	0 m/min	0 mm	0 mm
N1 Copper Alloys	0 m/min	0 m/min	0 mm	0 mm
N2 Low-Silicon Aluminium Alloys and Magnesium Alloys, Si <12,2%	0 m/min	0 m/min	0 mm	0 mm
N3 High-Silicon Aluminium Alloys , Si >12,2%	0 m/min	0 m/min	0 mm	0 mm
N4 Nylon, Plastics, Rubbers, Phenolics, Resins, Fibreglass	0 m/min	0 m/min	0 mm	0 mm
N5 Carbon, Graphite Composites, CFRP	0 m/min	0 m/min	0 mm	0 mm
S1 Iron-Based, Heat-Resistant Alloys	0 m/min	0 m/min	0 mm	0 mm
S2 Cobalt-Based, Heat-Resistant Alloys	0 m/min	0 m/min	0 mm	0 mm
S3 Nickel-Based, Heat-Resistant Alloys	0 m/min	0 m/min	0 mm	0 mm
S4 Titanium and Titanium-based Alloys	0 m/min	0 m/min	0 mm	0 mm
H1 Hardened Steel C0.2% - C0.8%	0 m/min	0 m/min	0 mm	0 mm
H2 Hardened Steel C0.8% - C2.1%	0 m/min	0 m/min	0 mm	0 mm

Turning - imperial starting values

Material	v_{c max}	v_{c min}	f_max	f_min
P1 Low Carbon Steel	492 SFM	295 SFM	0.0157 IPR	0.0024 IPR
P2 Alloy Steel	394 SFM	197 SFM	0.0098 IPR	0.0024 IPR
P3 Tool Steel	295 SFM	164 SFM	0.0098 IPR	0.0024 IPR
P4 Alloy Tool Steel	0 SFM	0 SFM	0 IPR	0 IPR
P5 Alloy Cast Steel	0 SFM	0 SFM	0 IPR	0 IPR
M1 Stainless Steel	0 SFM	0 SFM	0 IPR	0 IPR
M2 Stainless Steel - Austenitic, Martensitic	0 SFM	0 SFM	0 IPR	0 IPR
K1 Grey Cast Iron	0 SFM	0 SFM	0 IPR	0 IPR
K2 Cast Iron Malleable	0 SFM	0 SFM	0 IPR	0 IPR
N1 Copper Alloys	0 SFM	0 SFM	0 IPR	0 IPR
N2 Low-Silicon Aluminium Alloys and Magnesium Alloys, Si <12,2%	0 SFM	0 SFM	0 IPR	0 IPR
N3 High-Silicon Aluminium Alloys , Si >12,2%	0 SFM	0 SFM	0 IPR	0 IPR
N4 Nylon, Plastics, Rubbers, Phenolics, Resins, Fibreglass	0 SFM	0 SFM	0 IPR	0 IPR
N5 Carbon, Graphite Composites, CFRP	0 SFM	0 SFM	0 IPR	0 IPR
S1 Iron-Based, Heat-Resistant Alloys	0 SFM	0 SFM	0 IPR	0 IPR
S2 Cobalt-Based, Heat-Resistant Alloys	0 SFM	0 SFM	0 IPR	0 IPR
S3 Nickel-Based, Heat-Resistant Alloys	0 SFM	0 SFM	0 IPR	0 IPR
S4 Titanium and Titanium-based Alloys	0 SFM	0 SFM	0 IPR	0 IPR
H1 Hardened Steel C0.2% - C0.8%	0 SFM	0 SFM	0 IPR	0 IPR
H2 Hardened Steel C0.8% - C2.1%	0 SFM	0 SFM	0 IPR	0 IPR

Milling - metric starting values

Material	v_{c max}	v_{c min}	f_{z max}	f_{z min}
P1 Low Carbon Steel	0 m/min	0 m/min	0 mm	0 mm
P2 Alloy Steel	0 m/min	0 m/min	0 mm	0 mm
P3 Tool Steel	0 m/min	0 m/min	0 mm	0 mm
P4 Alloy Tool Steel	0 m/min	0 m/min	0 mm	0 mm
P5 Alloy Cast Steel	0 m/min	0 m/min	0 mm	0 mm
M1 Stainless Steel	0 m/min	0 m/min	0 mm	0 mm
M2 Stainless Steel - Austenitic, Martensitic	0 m/min	0 m/min	0 mm	0 mm
K1 Grey Cast Iron	0 m/min	0 m/min	0 mm	0 mm
K2 Cast Iron Malleable	0 m/min	0 m/min	0 mm	0 mm
N1 Copper Alloys	0 m/min	0 m/min	0 mm	0 mm
N2 Low-Silicon Aluminium Alloys and Magnesium Alloys, Si <12,2%	0 m/min	0 m/min	0 mm	0 mm
N3 High-Silicon Aluminium Alloys , Si >12,2%	0 m/min	0 m/min	0 mm	0 mm
N4 Nylon, Plastics, Rubbers, Phenolics, Resins, Fibreglass	0 m/min	0 m/min	0 mm	0 mm
N5 Carbon, Graphite Composites, CFRP	0 m/min	0 m/min	0 mm	0 mm
S1 Iron-Based, Heat-Resistant Alloys	0 m/min	0 m/min	0 mm	0 mm
S2 Cobalt-Based, Heat-Resistant Alloys	0 m/min	0 m/min	0 mm	0 mm
S3 Nickel-Based, Heat-Resistant Alloys	0 m/min	0 m/min	0 mm	0 mm
S4 Titanium and Titanium-based Alloys	0 m/min	0 m/min	0 mm	0 mm
H1 Hardened Steel C0.2% - C0.8%	0 m/min	0 m/min	0 mm	0 mm
H2 Hardened Steel C0.8% - C2.1%	0 m/min	0 m/min	0 mm	0 mm

Milling - imperial starting values

Material	v_{c max}	v_{c min}	f_{z max}	f_{z min}
P1 Low Carbon Steel	0 SFM	0 SFM	0 IPT	0 IPT
P2 Alloy Steel	0 SFM	0 SFM	0 IPT	0 IPT
P3 Tool Steel	0 SFM	0 SFM	0 IPT	0 IPT
P4 Alloy Tool Steel	0 SFM	0 SFM	0 IPT	0 IPT
P5 Alloy Cast Steel	0 SFM	0 SFM	0 IPT	0 IPT
M1 Stainless Steel	0 SFM	0 SFM	0 IPT	0 IPT
M2 Stainless Steel - Austenitic, Martensitic	0 SFM	0 SFM	0 IPT	0 IPT
K1 Grey Cast Iron	0 SFM	0 SFM	0 IPT	0 IPT
K2 Cast Iron Malleable	0 SFM	0 SFM	0 IPT	0 IPT
N1 Copper Alloys	0 SFM	0 SFM	0 IPT	0 IPT
N2 Low-Silicon Aluminium Alloys and Magnesium Alloys, Si <12,2%	0 SFM	0 SFM	0 IPT	0 IPT
N3 High-Silicon Aluminium Alloys , Si >12,2%	0 SFM	0 SFM	0 IPT	0 IPT
N4 Nylon, Plastics, Rubbers, Phenolics, Resins, Fibreglass	0 SFM	0 SFM	0 IPT	0 IPT
N5 Carbon, Graphite Composites, CFRP	0 SFM	0 SFM	0 IPT	0 IPT
S1 Iron-Based, Heat-Resistant Alloys	0 SFM	0 SFM	0 IPT	0 IPT
S2 Cobalt-Based, Heat-Resistant Alloys	0 SFM	0 SFM	0 IPT	0 IPT
S3 Nickel-Based, Heat-Resistant Alloys	0 SFM	0 SFM	0 IPT	0 IPT
S4 Titanium and Titanium-based Alloys	0 SFM	0 SFM	0 IPT	0 IPT
H1 Hardened Steel C0.2% - C0.8%	0 SFM	0 SFM	0 IPT	0 IPT
H2 Hardened Steel C0.8% - C2.1%	0 SFM	0 SFM	0 IPT	0 IPT

Go back

All technology data are recommendations. Relevant know-how in the proper handling of cutting tools is not replaced by this platform. Feed rate and cutting depth must be chosen so that the chip section does not exceed a value that could damage the tool or machine and also pays enough attention to the stability of the tool and clamping.